Panlite Sheet Features

Impact Resistance

Panlite Sheet has the highest level of strength of any plastic-three hundred times stronger than glass of the same thickness, 30 times tougher than PMMA sheet. Whether called upon to absorb hammer strikes or falling rocks, Panlite's exceptional impact resistance makes it an ideal high-tech material.

Material Conformity

Panlite Sheet can be easily cut and drilled using regular factory tools. Complicated designs with many curved surfaces, thermobending, vacuum bending and cold forming are all possible.


Panlite Sheet has proven itself under extremes of heat and cold. Even after long term outdoor exposure it retains its strength and excellent surface appearance.

Flame Resistance

Panlite Sheet and Film have passed the UL94 combustibility tests conducted for 94VTM and 94V-2. Also, Panlite has a high oxgen index (O.I.) of over 25%, making it difficult to burn.


Weighing half as much as glass of the same thickness, Panlite Sheet's ease of use makes it an excellent construction material.


Panlite Sheet, with a light transmittance level above 85% (clear sheet type), boasts the same transparency and surface luster as glass.
(Optical property)

  • Light transmittance : 87 ~ 90% (5 ~ 1.5t)
  • Refractive index : ND (25°C) = 1.585

Temperature Resistance

Outstanding performance even under extremes of heat and cold. Practically no damage occurs to Panlite Sheet between -40°C and +125°C, giving the user an extraordinary range of options.

Thermal Conductivity

Panlite Sheet, with one-fourth the thermal conductivity of glass, effectively saves energy by storing both hot and cold temperatures due to its low heat radiation.

Electrical Insulating

Panlite Sheet has the strongest electrical insulating property of all plastics, with its widest applications seen in the electric and electronics industry.

Volume resistivity: 3 x 10 16
Dielectric breakdown voltage: 40kV/mm
Dielectric constant: 2.90 ~ 2.95

Dimensional Stability

Panlite Sheet dimensional stability is proven by its low degree of creep.

Sanitary Qualities

Panlite Sheet has passed the general standard "Synthetic Resin Instruments and Container Package" tests as developed under the Food Hygiene Law (Notification No. 20 of Ministry of Health and Welfare, 1982), and is safe for use around food.

Tested Items Results
Pb Acceptable
Cd Acceptable
Heavy metal Acceptable
Potassium Permanganate consumption Acceptable

Noise Reduction

Panlite effectively muffles high frequency noise, and is useful in combating noise pollution in areas where this problem exists.

More Information

  • Panlite Sheet & Film Specifications
  • Panlite Sheet & Film Properties
  • MR Sheet Surface Performance

The first company to commercially produce polycarbonate resin in Japan, Teijin Chemicals Ltd. is proud to introduce its product.

“Panlite”, in these pages. Since its introduction, Teijin Chemicals Ltd. has dedicated itself to a continual improvement of quality and development of applications utilizing Panlite, enjoying numerous success. Through these tireless efforts, Panlite has become widely accepted as one of the world’s premier engineering plastics.
Teijin Chemicals Ltd. pioneering spirit continues today, with our products widely used in fields ranging from precision machinery to housewares, from the automotive industry to advanced medical equipment. Panlite’s remarkable collection of qualities such as heat resistance, dimensional stability, impact strength and transparency make it an ideal choice to meet a variety of product needs. Our customers can rest assured that the superior quality for which Teijin Chemicals Ltd. products are known will always be the cornerstone of our company’s approach to business.

Teijin / 日本(帝人) (PC-1150 / 1151/2151) Basic properties (比較物性表)
Property (特性) Unit (単位) Test Method Meaursement Condition (测定条件) Panlite Sheet (树脂板)
PC-1150 PC-1151 PC-2151
Density (密度) kg/m3 ISO 1183 1,200 1,200 1,200
Water absorption rate (吸水率) % ISO 62 after immersion in water 23℃ x 24h(23℃水中24h) 0.2 0.2 0.2
Light transmission(透光率) % ISO 13468-1 Thickness(厚度) 1mm 89.8 89.8 89.8
Refractive Index (折射率) ASTM D542 1,585 1,585 1,585
Tensile modulus (拉伸弹性率 ) MPa ISO 527-1 and ISO 527-2 1mm/min 2,400 2,400 2,400
Tensile yield stress (拉伸屈服应力) MPa 50mm/min 61 61 61
Tensile yield (拉伸屈服伸长率) % 50mm/min 6 6 6
Tensile fracture designation distortion (拉伸断裂公称伸长率) % 50mm/min >50 >50 >50
Flexural modulus (弯曲弹性模量) MPa ISO 178 2mm/min 2,300 2,300 2,300
Flexural strength (弯曲强度) MPa 2mm/min 91 91 91
Charpy impact (夏式冲击强度) KJ/m2 ISO 179 notched (附触点) 76 76 76
Heat distortion temperature under load (荷重翘曲温度) ISO 75-1 and ISO 75-2 Load(荷重) 1.80MPa 129 129 129
Load(荷重) 1.80MPa 142 142 142
Vicat softening temperature (维卡特软化点) ISO 306 50℃/h 50N 149 149 149
Coefficient of linear expansion (线膨胀系数) x10-4/℃ ISO 11359-2 0.7 0.7 0.7
Specific inductive capacity (介电常数) IEC 60250 100Hz 3.1 3.1 3.1
1MHz 3 3 3
Dielectric loss tangent (介电损耗正切) x10-4 IEC 60250 100Hz 10 10 10
1MHz 90 90 90
Volume resistivity (体积电阻率) Ω.m IEC 60093 >1x1013 >1x1013 >1x1013
Surface resistivity (表面电阻率) Ω IEC 60093 >1x1015 >1x1015 >1x1015
Withstand voltage (耐电压) MV/m IEC 60243-1 Short time test (短时间法) 30 30 30
Tracking resistance (耐电弧径迹性) IEC 60112 250 250 250

※The list above shows measured values and not guaranteed values (上面列表所显示的测量值并非保证值)